Vacuum gas quenching
Vacuum gas quenching and vacuum oil quenching of mould, cutter, measuring tool, mechanical parts, sports equipment, automobile parts, etc. with the application of vacuum technology, oxidation and decarburization can be prevented, with less deformation, lower cracking tendency and good surface color.
Vacuum gas quenching and vacuum oil quenching are applied to prevent oxidation and decarburization, with less deformation, lower cracking tendency and better surface color.
Technical parameters: limit vacuum degree: 2.6*10-3Pa
Effective heating area: 800*800*1400mm
Maximum furnace charge: 1500kg
Gas quenching pressure: less than 1MPa.
Application: mold, cutting tools, measuring tools, mechanical parts, sports equipment, auto parts, etc.
Processing equipment:
fully automatic intellectualized original Swiss Solo (SOLO) Bell-Type Furnace Line, 1 Set.
Vacuum high pressure gas quenching furnace, 10 SETS.
Vacuum oil quenching gas cooling furnace, 1 SETS.
Chamber tempering furnace, 6 SETS.
Cryogenic unit, 2 Sets
Testing item: hardness (HRC)
Testing equipment: Rockwell hardness tester.
Advantages: heating under vacuum state, and cooling with high-purity nitrogen, which can realize the functions of no oxidation, no decarburization, no carburization, degreasing and degassing, so as to achieve the effect of surface bright purification. The parts, after vacuum heat treatment, the distortion is small, the quality is high, and the process itself is flexible and pollution-free.
Suitable for: high alloy mould steel quenching, high speed steel quenching, stainless steel solution aging, titanium alloy, nickel alloy solution aging, vacuum annealing, vacuum demagnetization, vacuum tempering, vacuum stress relief.
Price: calculated according to the type of workpiece
Delivery time: generally 3 working days, otherwise in special circumstances